Super hydrophilic self cleaning Coating for Anti-fog is Yellowish transparent liquid,used for anti-fog agent,Super hydrophilic self cleaning Coating for
Anti-fog is mainly used for windshields,Polyurethane PET film / PC / PMMA sheets etc.. It is also be widely used in car and glass field etc.
Feature
Strong hydrophilicity
Good adhesion
High hardness
Excellent water resistance
Good abrasion resistance
Wide adaptability
Qualification
Density（g/cm2） :0.8-1.0
Coating thickness（μm）: 5-8
Leveling temperature/time（℃）: 60℃/15min
UV Curing Energy（J/cm*cm）: 380-450
Application
PET film / PC / PMMA sheets
Super hydrophilic self cleaning Coating for Anti-fog
|
Testing items
|
Test method
|
Result
|
|
Initial droplet angle
|
3-5 ml water, 5 s test
|
< 5 degrees
|
|
Dry film adhesion
|
Berg test
|
Greater than 4B
|
|
Wet film adhesion
|
80 degrees steam fumigated nail scratch
|
Scratch free
|
|
hardness
|
Pencil Hardness Test (Acrylic Plate)
|
> 4H
|
|
Water test
|
Soak tap water at room temperature for 12 hours
|
< 10 degrees
|
|
Washing experiment
|
Wash and dry under the tap by hand and recycle 20 times.
|
< 10 degrees
|
HOW TO USE
Coating for Anti-fog
Pre-cleaning: To ensure that the surface of the substrate is clean and free from dirt.
Spraying process: A disposable dropper can be uniformly sprayed on the sample plate, then placed vertically, first at room temperature for 90 seconds, then 60 degrees infrared for 15 minutes, and then UV curing.
Curing process: Super hydrophilic self cleaning Coating for anti-fog requires uv curing, energy between 380-450 J/cm*cm for Anti-fog coating.
If you want to know more about Super hydrophilic self cleaning Coating for Anti-fog, please contact us Sinograce Chemical .