| Apprearance |
Milky white |
| Solid Content(%) |
33±1 |
| pH(25C°) |
7.0 - 9.0 |
| Viscosity(25C°，Mpa.s) |
<400 |
| Modulus(Mpa) |
0.5 |
| Elongation% |
1100 |
| Tensile Srtrength(Mpa) |
2.5 |
1.Toluene and Ketone-Free: Environmentally friendly and safe for diverse applications.
2.Film Forming (33% Solid): Ensures consistent and smooth application.
3.Aliphatic Composition: Provides superior durability and resistance.
4.Mono Resin Formulation: Tailored for ink formulations to simplify processing.
5.High-Speed Compatibility: Optimized for high-press-speed operations.
6.Fully Water Reducible: Environmentally friendly with drying adjustments as needed.
7.Polyurethane dispersion with excellent Transfer Property: Delivers vibrant and consistent print quality.
8.Waterborne Polyurethane resin with anti-Blocking Properties: Prevents sticking during processing.
9.Retort Grade: Suitable for retort applications (consult technician for details)
Waterborne polyurethane binder suitable For Wood coatings, industrial paints, leather finishes, and package printing,textile printing etc
Waterborne polyurethane resin stored at 20°C for 6 months after delivery date. The recommended temperature range is 5~30 oC. Freezing or storage at higher temperature than 30°C, can affect the viscosity or the average particle size and finally lead to a sedimentation or coagulation. A contamination with bacteria, fungi or algae can damage the product irreversible